Apakah Kekerasan Air Maksimum Yang Dibenarkan (Ppm CaCO₃) Untuk Pemanas Sarung Titanium Gred 7 Dalam Larutan Natrium Tripolifosfat 5% Pada 90 darjah Untuk Mengelakkan Skala Kalsium Fosfat-Terlalu Panas?
Tinggalkan pesanan
In 5% sodium tripolyphosphate (STPP) at 90°C, calcium ions precipitate as calcium phosphate (Ca₃(PO₄)₂) scale. This scale has low thermal conductivity (0.3–0.6 W/m·K). The maximum allowable water hardness (as CaCO₃) to prevent overheating is 100 ppm. Above 100 ppm, scale thickness exceeds 0.2 mm within 500 hours, causing >30% pengurangan pemindahan haba.
Pembentukan Skala Kuantitatif lwn Kekerasan Air
Dalam 5% STPP pada 90 darjah selama 500 jam:
| Kekerasan (ppm CaCO₃) | Ketebalan Skala (µm) | Komposisi Skala | Pengurangan Pemindahan Haba (%) |
|---|---|---|---|
| 0 | 0 | tiada | 0 |
| 50 | 10–30 | Kalsium fosfat | 5–15 |
| 100 | 30–70 | Kalsium fosfat | 15–30 |
| 150 | 60–120 | Kalsium fosfat padat | 25–45 |
| 250 | 100–200 | Skala berat | 40–60 |
| 500 | 200–400 | Skala teruk | 60–80 |
Kesan Kepekatan dan Suhu STPP
| STPP (%) | Suhu (darjah) | Kekerasan Maks untuk<0.1 mm Scale (ppm) |
|---|---|---|
| 3 | 90 | 150 |
| 5 | 80 | 150 |
| 5 | 90 | 100 |
| 5 | 100 | 60 |
| 10 | 90 | 50 |
Panduan Kawalan Kekerasan Air
| Kekerasan (ppm CaCO₃) | Tindakan yang Disyorkan | Ketebalan Skala Jangkaan (µm/tahun) |
|---|---|---|
| <50 | tiada | <30 |
| 50–100 | Pantau setiap bulan | 30–70 |
| 100–150 | Gunakan air lembut | 70–120 |
| >150 | Pelembut air diperlukan | >120 |
Syor Kejuruteraan
Untuk perkhidmatan STPP pada 90 darjah, kekalkan kekerasan air di bawah 50 ppm menggunakan pelembut air. Dengan mengawal kepekatan kalsium, jurutera menghalang pembentukan skala kalsium fosfat dan terlalu panas.